The Si-PET/F-silica/CB coating was prepared by spraying a dispersion consisting of F-silica, Si-PET adhesive and photothermal CB nanoparticles onto Al alloy plates and thermal curing. The coating shows excellent superhydrophobicity, impalement resistance, mechanical robustness and weather resistance. Moreover, the coating also shows excellent passive anti-icing and active de-icing performance in low temperature, high relative humidity, and weak sunlight environment.

Abstract

Photothermal superhydrophobic coatings hold great promise in addressing the limitations of conventional superhydrophobic anti-icing coatings. However, developing such coatings with excellent impalement resistance, mechanical robustness and weather resistance remains a significant challenge. Here, we report facile preparation of robust photothermal superhydrophobic coatings with all the above advantages. The coatings were prepared by spraying a dispersion consisting of fluorinated silica nanoparticles, a silicone-modified polyester adhesive and photothermal carbon black nanoparticles onto Al alloy plates followed by thermal curing. Thermal curing caused migration of perfluorodecyl polysiloxane from within the coatings to the surface, effectively maintaining a low surface energy despite the presence of the adhesive. Therefore, combined with the hierarchical micro-/nanostructure, dense yet rough nanostructure, adhesion of the adhesive and chemically inert components, the coatings exhibited remarkable superhydrophobicity, impalement resistance, mechanical robustness and weather resistance. Furthermore, the coatings demonstrated excellent photothermal effect even in the −10 °C, 80 % relative humidity and weak sunlight (0.2 sun) environment. Consequently, the coatings showed excellent passive anti-icing and active de-icing performance. Moreover, the coatings have good generalizability and scalability. We are confident that this study will accelerate the practical implementation of photothermal superhydrophobic coatings.